Low Carbon Cr19ni10 Stainless Steel Welding Electrodes E308L-16

• Type: S (Chromium Nickel Austenitic Stainless Steel Electrode)
• Material: Stainless Steel
• Diameter: 3.2mm
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: AWS E308L-16
• Length: 300-400mm
• Welding Core Type: Stainless Steel
• Electrode Coating Type: Titanium Calcium
• Slag Characteristic: Alkaline
• Stainless Steel Welding Rod Type: Chromium Nickel Stainless Steel
• Function: Surfacing Electrode, Low Hydrogen Type Electrode, High Efficient Iron Powder Electrode
• Welding Power: AC/DC
• Transport Package: 5kg/Box, 20kg/Carton
• Specification: 3.2mm x 350mm
• Trademark: TY
• Origin: China
• HS Code: 8311100000
• Production Capacity: 10000kg/Day
• Package Size: 5.00cm * 5.00cm * 400.00cm
• Package Gross Weight: 5.000kg

Product Description

Stainless Steel Welding Electrodes

AWS E308L-16(A002)


Description:
AWS E308L-16 is a super-low carbon Cr19Ni10 stainless steel type electrode coated Titianum-calcium.The molten metal content is ≤0.04%.It provides excellent performance of intorcry stalline corrosion resistance.It has excellent operational technological performance on both AC and DC.


Application:
It applies to welding the structure of super-low carbon Cr19Ni10 stainless steel.It also suitable for welding the structure of anti-corrosion stainless steel 0Cr19NillTi which working temperature below 300ºC. It is mainly used for equipment manufacturing of fibre,fertilizer and petroleum industry.

 

Chemical Composition Deposited Metal (%)
C	Mn	Si	Cr	Ni	S	P	Mo	Cu
≤0.04	0.5-2.5	≤0.90	≤18-21	9-11	≤0.03	≤0.04	≤0.75	≤0.75

 

Mechanical Properties of Deposited metal
Test Item	Tensile Strength ós (Mpa)	Elongation δ5(%)
Guranteed	≥520	≥35

 

Sizes & Recommended Current (AC or DC)
Welding rod diameter  (mm)	2.0	2.5	3.2	4.0	5.0
welding current (A)	25-50	50-80	80-110	110-160	160-200

Notes:

1. Electrodes must be baked for 1 hour at 150ºC before welding operation.
2. To operate on DC if all possible.Operate with small current so the electrode will not in red-hot.
3. The anti-corrosion performance and ferrite composition should be detemined between buyer and seller.

 

  Packing & Delivery

 

 

 

Size: 2.5mm*300mm,
package: 5.0 kg/inner box, 4 boxes/ carton=20kg,

Size: 3.2mm*350mm,
package: 5.0 kg/inner box, 4 boxes/ carton=20kg,

Size: 4.0mm*400mm,
package:5.0 kg/inner box, 4 boxes/ carton=20kg.

1000kgs (50cartons)/pallet

 

   FAQ

 

Q: what is delivery time / lead time ?

A: 2-3weeks.

Q: what is your minimum order ?

A: 3000kgs/each size.

Q: what is your payment term ?

A: 50% T/T in advance, 50% balance paid before shipment.

Q: can we visit your factory ?

A: Yes, welcome to our factory at any time.