Welding Carbon Electrodes Steel Rod Metal Aws E6013 6013 E7018 7018 E6011 E6010 E6018 E7016

• Customization: Available
• Type: E (Carbon Steel Electrodes/ Low Alloy Steel Electrodes)
• Material: Carbon Steel
• Diameter: 2.5mm, 3.2mm, 4.0mm, 5.0mm
• Length: 300mm, 350mm, 400mm
• Welding Core Type: Carbon Structural Steel
• Electrode Coating Type: High Cellulose Potassium
• Slag Characteristic: Acidic
• Stainless Steel Welding Rod Type: Carbon Steel
• Function: High Efficient Iron Powder Electrode, Gravity Electrode, Moisture-Proof Electrode
• Welding Power: AC and DC
• Service: OEM Service
• Advantage 1: Quick Strike & Easy Restrike & Easy Slag-Removal
• Advantage 2: Stable Arc Performance & Minimal Arc Interference
• Advantage 3: Smooth and Shiny Appearance
• Advantage 4: Excellent Mechanical Properties
• Advantage 5: High Efficiency and High Impact Values at -30c.
• Advantage 6: High Deposition Rates
• Transport Package: 5kg/Box, 20kg/CTN, 1000kg/Pallet
• Trademark: TUYE
• Origin: China
• HS Code: 8311100000
• Production Capacity: 5000000 Ton/Year

Product Description

Product Description

Aws E6010 E6011 Factory Manufacturing Welding Electrode 2.5mm 3.2mm 4.0mm

Application:
It applies to butt welding, fillet welding, and overlap welding of thin steel plates such as oil tanks of transformers, vessel hull, and vehicle crust low carbon steel structures for flue and venting tubes.
 

Chemical Composition Deposited Metal (%)
C	Mn	Si	S	P
≤0.12	0.3-0.6	≤0.35	≤0.035	≤0.040

 

Mechanical Properties of Deposited metal
Test Item	Tensile Strength ós (Mpa)	Yield Strength ós (Mpa)	Elongation δ5(%)	Impact Value (J)-30°C
Guranteed	≥420	≥330	≥17	≥27
Tested	480-580	≥340	18-26	100-130

X-ray Radiographic Inspection:  II Grade
 

Sizes & Recommended Current (AC or DC)
Welding rod diameter  (mm)	2.0	2.5	3.2	4.0	5.0
welding current (A)	25-40	30-50	70-100	90-140	150-200

Description:
E6010 E6011 is cellulose Sodium coated type electrode specialized in vertical-down welding of carbon steel. The weld of vertical-down is neat andsmooth. It can be operated on both AC and DC. Less swing and proper level is required when welding.

Notes
1.  The defects of less rigidity pars in small thin-wall cast iron pieces can be welded without  preheating, but general weldments need to be preheated up to around 400°C. If the weldmentspreserve heat and slowly cool down, they are on the cards that the soldering joints can bearcut processing.
2.  These welding rods are not suitable for the important castings that bear the stress and impact, etc.
3.  The weld rods should be baked at around 150°C for an hour before the start of welding operation.

-------------------Our Other Welding Products-------------------
If you are interested, please click on the below picture to enter the link

 

.

 

  Packing & Delivery

 

 

 

Size: 2.5mm*300mm,
package: 5.0 kg/inner box, 4 boxes/ carton=20kg,

Size: 3.2mm*350mm,
package: 5.0 kg/inner box, 4 boxes/ carton=20kg,

Size: 4.0mm*400mm,
package:5.0 kg/inner box, 4 boxes/ carton=20kg.

1000kgs (50cartons)/pallet

 

   FAQ

 

Q: what is delivery time / lead time ?

A: 2-3weeks.

Q: what is your minimum order ?

A: 5000kgs/each size.

Q: what is your payment term ?

A: 50% T/T in advance, 50% balance paid before shipment.

Q: can we visit your factory ?

A: Yes, welcome to our factory at any time.