Aws E7014 J501fe Carbon Steel Welding Electrodes

• Type: E (Carbon Steel Electrodes/ Low Alloy Steel Electrodes)
• Material: Low Hydrogen Potassium
• Diameter: 3.2mm
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: E7014
• Length: 300-400mm
• Welding Core Type: Carbon Structural Steel
• Electrode Coating Type: Carbon Structural Steel
• Slag Characteristic: Acidic
• Function: Low Hydrogen Type Electrode, Moisture-Proof Electrode, Vertical-Down
• Welding Power: AC/DC
• MOQ: 1000kg
• Transport Package: Carton
• Specification: 5kg/box, 20kgs/carton
• Trademark: TYUE
• Origin: Wenzhou
• HS Code: 8311100000
• Production Capacity: 10 Ton
• Package Size: 35.00cm * 29.00cm * 9.50cm
• Package Gross Weight: 5.150kg

Product Description

AWS E7014 J501fe carbon Steel Welding Electrodes

Carbon Steel Electrodes E7014 is a high titania type electrode containing iron powder in its coating and is suitable for all position high efficient welding.

As the contact welding can be performed with this electrode, manipulation of electrodes is easy in horizontal fillet or in the groove.
It is also used in vertical downward welding.
Slag detachability is good and it deposits weld metal of lustrous and good appearance.

Application:
This electrode is suitable for all types of carbon steel fabrications, particularly in horizontal fillet
welding of sheet metal and ornamental iron work.

Characteristics on Usage:
S-7014.F is an iron powder electrode for high speed all position welding. As the contact welding can be performed with this electrode, manipulation of electrodes is easy in horizontal fillet or in the groove.

Notes on Usage:
In the case of vertical downward welding, manipulate the electrode, keeping its tip in contact with mother plate as shown in the sketch.
Pay attention not to exceed the range of proper currents.
Welding with excessive current not only lowers X-ray performance, but also causes increase of spatter, undercut and insufficient slag covering.
Dry the electrodes at 70-100ºC for 30-60 minutes before use.
Excessive moisture absorption lowers usability and may result in some porosity.

Current:
DC or AC ±

TYPICAL CHEMICAL COMPOSITION OF WELD METAL (%):

C	Mn	Si	P	S
0.08	0.58	0.35	0.015	0.011

TYPICAL MECHANICAL PROPERTIES OF WELD METAL:

Yield Point	Tensile Strength	Elongation	Impact Value
N/mm^2 (ksi)	N/mm^2 (ksi)	%	°C, J (°F, Ft-Lbs)
470 (68)	550 (80)	25	-29°, 60 (-20°, 44)

WELDING POSITIONS: ALL POSITIONS
SIZES AVAILABLE AND RECOMMENDED CURRENTS (AC or DC + ):

Diameter (mm		3.2	4	5
Length (mm)		350	400	400
A	F	95-140	140-200	180-250
	V, O	90-130	120-170	140-200