Aws E308L-16 Arc Welding S. S. Welding Electrodes Aws E308-16 Stainless Steel Rods

• Type: S (Chromium Nickel Austenitic Stainless Steel Electrode)
• Material: Stainless Steel
• Diameter: 2.5-4.0mm
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: E308L-16
• Length: 300-400mm
• Welding Core Type: Stainless Steel
• Electrode Coating Type: Titanium Calcium
• Slag Characteristic: Acidic
• Stainless Steel Welding Rod Type: Chromium Nickel Stainless Steel
• Function: Surfacing Electrode, Low Hydrogen Type Electrode, Hardfacing Electrode, High Efficient Iron Powder Electrode, Gravity Electrode, Moisture-Proof Electrode, Stainless Electrode
• Welding Power: DC/AC
• Transport Package: 5kg/Box, 20kg/Carton
• Specification: 2.5mm/3.2mm/4.0mm
• Trademark: TYUE
• Origin: China
• HS Code: 831110000
• Production Capacity: 5000000 Ton/Year
• Package Size: 100.00cm * 100.00cm * 120.00cm
• Package Gross Weight: 1050.000kg

Product Description

WENZHOU TIANYU ELECTRONIC CO., LTD.

Stainless Steel Welding Electrode/Rod

AWS A5.4 E308L-16
GB/T 983 E308L-16
ISO 3581-B-ES308L-16

APPLICATIONS:
It is suitable for welding low carbon 00cr18ni9 stainless steel structure, also can be used to the corrosion resistance of stainless steel structure,such as the 0cr19ni11ti, whose working temperature below 300 ºC, it is mainly used for manufacture of synthetic fiber, fertilizer, oil and other equipment.

FEATURES:
AWS E308L-16 is a coated rutile type of ultra-low carbon Cr18Ni9 stainless steel electrode.Both AC and DC can be used and can be all-position welding. It can reach  excellent welding performance, stable arc, little spatter, easy slag removal and good weld appearance. The deposited metal has good resistance to intergranular corrosion.

ATTENTION:
1.Electrode must be approved by 320-350 ºC for 1 hour before welding, dry the electrode when use it.
2. The rust, oil, water and other impurities of the weld must be removed before welding.
3.Recommended DC power supply, because AC welding has a shallow penetration, the current should not be too large, in order to avoid the coating redness and cracking.
4. To minimize the amount of heat input and welding electrode oscillating amplitude shoulds not be too big.
5.Preheat and interlayer-temperature should remain below 150 ºC

WELDING POSITIONS:
PA, PB, PC, PD, PE, PF

SIZE:
2.0*300mm(350mm)
2.5*300mm(350mm)
3.2*350mm
4.0*350mm(400mm)

PACKING:
5kg/inner box,
20kg (4box)/outer carton,
1000kgs=1ton=50cartons packed on a pallet.


SPECIFICATION  DATA:  
 

Chemical Composition Deposited Metal (%)
C	Mn	Si	Cr	Ni	S	P	Mo	Cu
≤0.04	0.5~2.5	≤0.90	≤18~21	9~11	≤0.03	≤0.04	≤0.75	≤0.75

 

Mechanical Properties of Deposited metal
Test Item			Tensile Strength ós (Mpa)			Elongation δ5(%)
Guranteed			≥520			≥35

 

Sizes & Recommended Current (AC or DC)
Welding rod diameter (mm)	2.0	2.5	3.2	4.0	5.0
welding current (A)	25~50	50~80	80~110	110~160	160~200

PRODUCT PICTURE:


  

 

 

   FAQ

 

Q: What is delivery time / lead time ?

A: 2-3 weeks.

Q: What is your minimum order ?

A: 3000kgs/each size. (MOQ for stainless steel welding electrode)

Q: What is your payment term ?

A: 50% T/T in advance, 50% balance paid before shipment.

Q: Can we visit your factory ?

A: Yes. Welcome to visit our factory at any time.
Q: Can you provide free sampe ?
A: Yes. Free samples are available for you.