Stainless Steel Welding Electrodes Aws E308L-16 Welding Rod

• Type: Stainless Steel Welding Electrodes
• Material: Stainless Steel
• Diameter: 2.5mm
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: E308-16, E308L-16, E309-16, E309L-16
• Length: 300-400cm
• Welding Core Type: Stainless Steel
• Electrode Coating Type: Titanium Calcium
• Slag Characteristic: Acidic
• Stainless Steel Welding Rod Type: Chromium Stainless Steel
• Function: Low Hydrogen Type Electrode, Gravity Electrode, Moisture-Proof Electrode
• Welding Power: AC/DC
• Transport Package: Carton
• Specification: 5kgs/inner box, 20kgs/outer carton
• Trademark: TYUE
• Origin: China
• HS Code: 8311100000
• Production Capacity: 500000000ton/Year
• Package Size: 100.00cm * 100.00cm * 120.00cm
• Package Gross Weight: 1050.000kg

Product Description

Product Description

E308L-16 Stainless Steel Welding Electrode/Rod 
 

Description:

A002 is a super-low carbon Cr19Ni10 stainless steel type electrode coated with Titanium-calcium.The molten content is ≤0.04%.It provides excellent performance of intorcry stalline corrosion resistance.It has excellent operational technological performace on both AC and DC.

Application:

It applies to welding the structure of super-low carbon Cr19Ni10 stainless steel.It also suitable for welding the structure of anti-corrosion stainess steel 0Cr19NillT1 which working temperature below 300ºC.It is mainly used for equipment manufacturing of fibre,fertilizer and petroleum industry.
 

Chemical Composition Deposited Metal (%)
C	Mn	Si	Cr	Ni	S	P	Mo	Cu
≤0.04	0.5~2.5	≤0.90	≤18~21	9~11	≤0.03	≤0.04	≤0.75	≤0.75

 

Mechanical Properties of Deposited metal
Test Item			Tensile Strength ós (Mpa)			Elongation δ5(%)
Guranteed			≥520			≥35

 

Sizes & Recommended Current (AC or DC)
Welding rod diameter (mm)	2.0	2.5	3.2	4.0	5.0
welding current (A)	25~50	50~80	80~110	110~160	160~200

Notes:

1.Electrodes must be baked for 1 hour at 150ºC before welding operation.
2.To operate on DC if all possible.Operate with small current so the electrode will not in red-hot.
3.The anti-corrosion performance and ferrite composition should be detemined between buyer and seller

 

 