Product Description
Tyue Aws Enife-C1 Cast Iron Welding Electrode/Rod 3.2*350mm
The welding electrode/rod is Suitable for repairing or surfing cracked and worn parts made of gray cast iron or ncdular iron,
as well as joining cast iron with dissimilar metals.It is machinable.
Details about the Cast Iron Welding Electrode/Rod (AWS ENIFE-C1)
Model Number: aws enife-c1 cast iron welding rod
Material: Cast Iron welding rod
Length: 300mm-500mm
Diameter: 2.5mm 3.2mm 4.0mm
Application: All grades of castings, Pumps casing, gear housing, Engine blocks
Features of welding rod
1) Pure nickel core
2) Strong reducing property
3) Graphite type welding rod
4) Weldment: No need to preheat, good crack resistibility and process-ability
5) Both AC and DC applicable
6) Relatively expensive
7) Used for welding thin cast iron piece and repairing welding
Surfaces, such as the cast iron parts of cylinder covers,
Engine bases, gearcases and lathe guide rails.
Mechanical Properties of Deposited Metal
Tensile Strength N\mm2 ≥520
(HV) 170-220
Description
An all position Medium heavy coated, graphite based cast iron electrodes. It deposits Nickel and Iron alloy weld metal, which is ductile and machineable, joining various types of cast Iron including nodular cast iron.
Applications for welding rod
The cast iron welding rod is used for joining for non-ferrous and ferrous material, Heavy castings where machinability is required, Repair of broken castings, Engine heads, Pumps casing, ingot moulds.
Our advantages
stable arc, little spatter, less smoke;
higher deposition efficiency;
excellent welding performance;
easy restrike.
Z208
Z208 Cast Iron Welding Electrode
Accord with:GB/T 10044 EZC
Description:
Z208 is a graphitic type coating cast iron electrode with carbon steel core. Both AC and DC can be applied in welding. Weld seam metal has excellent crack resistibility. And its price is cheaper.
Applications:
It is used for repairing welding defects for gray cast iron.
Chemical Composition of Deposited Metal: (%)
| |
C |
Mn |
Si |
S |
P |
Fe |
| Standard |
2.00-4.00 |
≤0.75 |
2.50-6.50 |
≤0.10 |
≤0.15 |
The rest |
| Typical |
2.70 |
0.40 |
4.20 |
0.006 |
0.020 |
|
Recommended Current (AC or DC)
| Size(mm) |
2.5*300 |
3.2*350 |
4.0*400 |
5.0*400 |
| Current(A) |
60-90 |
90-120 |
150-180 |
190-220 |
Attention:
a. welding electrodes must be baked for 1 hour at the temperature of 150ºC before welding.
b. For cast iron parts bearing impact stress, it is not good to use it.
c. For welding detects of small and thin cast iron parts fabricated by low steel, welding electrodes need not be preheated. For general welding pipes, welding electrodes should be preheated to around 400ºC, cool it after welding and the welding zone may be processed by cutting.
Z308
Z308 Cast Iron Welding Electrode
Accord with:GB/T 10044 EZNi-1
Equivalent norm: AWS A5.15 ENi-C1
Description:
Z308 is a covered welding electrode with pure nickel core and graphitic coating for cast iron. The Weld seam metal has excellent machinability and crack resistibility. Both AC and DC can be applied.
Applications:
It is used for repairing welding thin pieces and processing surface of cast iron, as well as important grey cast iron pieces, such as engine gear box, machining tools, guideway, etc
Chemical Composition of Deposited Metal: (%)
| |
C |
Mn |
Si |
S |
Ni |
Fe |
Others |
| Standard |
≤2.0 |
≤1.0 |
≤2.50 |
≤0.03 |
≥90 |
≤8.0 |
≤1.0 |
| Typical |
0.59 |
0.07 |
1.50 |
0.004 |
94 |
0.021 |
|
Recommended Current (AC or DC)
| Size(mm) |
2.5*300 |
3.2*350 |
4.0*400 |
5.0*400 |
| Current(A) |
60-90 |
90-110 |
120-150 |
150-180 |
Attention:
a. welding electrodes must be baked for 1 hour at the temperature of 80-120ºC before welding.
b. Hammering the welded seam to dispel stress around the welding region and to avoid cracking.
c. Large current should be avoided in cold welding for cast iron, so as to reduce impurities of base metal to penetrate the weld seam and to reduce the width of the weld zone, and then to improve the ability of crack-resistance and capability of machine processing of the weld seam.
Z408
Z408 Cast Iron Welding Electrode
Accord with:GB/T 10044 EZNiFe-1
Equivalent norm: AWS A5.15 ENiFe-C1
Description:
Z408 is a graphitic (with strong reducing) type coating with Ni/Fe core welding electrodes for cast iron. It has features as follows: high toughness, excellent plasticity, low linear expansion coefficient, etc. Both AC and DC can be applied with welding.
Applications:
It is used for repairing welding important and high-toughness parts made of cast iron and modular iron, such as cylinder head, motor stand, gear wheel, etc.
Chemical Composition of Deposited Metal: (%)
| |
C |
Mn |
Si |
S |
Ni |
Fe |
Al |
Cu |
| Standard |
≤2.0 |
≤2.5 |
≤4.0 |
≤0.03 |
45-60 |
The rest |
≤1.0 |
≤2.50 |
| Typical |
0.70 |
0.24 |
1.00 |
0.006 |
54 |
0.06 |
0.054 |
0.054 |
Recommended Current (AC or DC)
| Size(mm) |
2.5*300 |
3.2*350 |
4.0*400 |
5.0*400 |
| Current(A) |
50-80 |
80-110 |
110-140 |
150-180 |
Attention:
a. welding electrodes must be baked for 1 hour at the temperature of 150ºC before welding.
Size: 2.5mm*300mm,
package: 5.0 kg/inner box, 4 boxes/ carton=20kg,
Size: 3.2mm*350mm,
package: 5.0 kg/inner box, 4 boxes/ carton=20kg,
Size: 4.0mm*400mm,
package:5.0 kg/inner box, 4 boxes/ carton=20kg.
1000kgs (50cartons)/pallet
Q: What is delivery time / lead time ?
A: 2-3weeks.
Q: What is your minimum order ?
A: 300kgs/each size. (MOQ for cast iron welding electrode)
Q: What is your payment term ?
A: 50% T/T in advance, 50% balance paid before shipment.
Q: Can we visit your factory ?
A: Yes. Welcome to our factory at any time.
Q: Can you provide free sampe ?
A: Yes. Free samples are available for you.
Audited Supplier 
){kind=link}