Submerge Arc Solid Solder Coil Nail Copper Welding Wire

• Type: Rolling Wire
• Material: Low Carbon Steel
• Flux Containing: Not Containing Flux
• Slag Characteristic: Acidic
• Extended Length: 10-20mm
• Typee: Solid Gas Shield
• OEM: Accept
• Feature: Stable Feasibility
• Package: Caron, Drum
• Color: Copper Coated
• Transport Package: D200& D270& D300 Plastic Spool+Box+Pallet
• Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
• Trademark: TYUE
• Origin: China
• HS Code: 72292000
• Production Capacity: 1000ton/Month

Product Description

Submerge Arc Solid Solder Coil Nail Copper Welding Wire

Submerge Arc Solid Solder Coil Nail Copper Welding Wire
1. Description: 
1)The weld metal shows a Fine appearance.
2) Both AC and DC can be applied.
3)Stable Arc
4)Easily removable residue

The products easily removable residue, good seam forming and highly efficient deposiyion. Wire meltingdoes not lead to splash or strong flasing. The sem surface is smooth and welding quality is guaranteed. They facilitate mechanical and automatic welding process. With a wide range of welding parameters, the wires can be used in open fields with strong wind and applied to automobiles, ships, bridg es and chemical engineering.
 

Main Applications:
It is suitable to weld 450Mpa-500Mpa grade structures, such as boilers, ships, bridg es, pressure vessels, as well as LPG cylinders, Before welding, the base metal must clear away impurities and fht flux must be baked in a temperature of 300° C-350° C for 1-2 hours.

Mechanical  Property
Joint  Strength                 (MPA)δ	succumb  strength     (MPA)  δ 0.2	elongation  index                   δ 5%	shock  value             Akv             -20  (J)
560	480	30	105
Chemical  Composition
C	Mn	Si	S	P		Other
0.07%	0.95%	0.03%	0.010%	0.012%		≤ 0.50
Procedure& Package
Dia	2.0mm	2.5mm	3.0mm	3.2mm	4.0mm	5.0mm
Current	300-400	350-450	400-500	425-525	475-575	550-650
Voltage	26-29	27-30	27-30	27-30	27-30	27-30
Weight/spool(KG)	25	25	25	25	25	25