Tyue Brand Aws 5.20 E71t-GS Flux Cored Gasless Welding Wire No Gas or MIG Steel Welding Wire 0.8mm/1.0mm/1.2mm/1.6mm

• Customization: Available
• Type: Flux-cored Wire
• Material: Carbon Steel
• Model NO.: E71T-11, E71T-GS
• Flux Containing: Containing Flux
• Slag Characteristic: Acidic
• Extended Length: 10-20mm
• Specification: 0.8/0.9/1.0/1.2/1.4/1.6/2.0/2.4mm
• Trademark: TYUE
• Origin: China
• HS Code: 8311200000
• Production Capacity: 500000000ton/Year
• Package Size: 100.00cm * 100.00cm * 120.00cm
• Package Gross Weight: 15.500kg

Product Description

Wenzhou Tinayu Electronic Co., Ltd.

High Quality CO2 Gas shielded flux-cored welding wire


Model No: E71T-11, E71T-GS, E71T-1
Conforms to: AWS  A5.20/ASME SFA A5.20 
Diameter::0.8 0.9 1.0 1.2 1.6mm
Free sample OEM approved
Weld Process: Mig Welding Process
Application: for all position
Brand: Tyue

Product Description:
E71T serie sis a kind of TI type flux cored wire for CO2 welding. It has high cladding efficiency, good welding technical performance in  all-position welding, apply for low carbon steel and 500MPA grade strength  steel welding, such as Industry of Metallurgical, Building,  Chemical, shipping, pressure vessels, mechanical equipments.

Packing & Delivery:  AWS A5.20 E71T-1C, E71T-11,  E71T-GS 
Size(MM) × Weight (KG)
0.8MMX1KG/SPOOL, 
0.8MMX5KG/SPOOL, 
0.8MMX15KG/SPOOL, 
 
0.9MMX1KG/SPOOL, 
0.9MMX5KG/SPOOL, 
0.9MMX15KG/SPOOL,
 
1.0MMX1KG/SPOOL, 
1.0MMX5KG/SPOOL, 
1.0MMX15KG/SPOOL, 
 
1.2MMX1KG/SPOOL, 
1.2MMX5KG/SPOOL, 
1.2MMX15KG/SPOOL, 

 
Advantage
• All-position with stable arc less splash
• Less welding smoke, shaped good appearance, high welding efficiency
• Inherent quality stable and reliable,good mechanical property of deposited metal
• Manufactured under a quality system certified to ISO 9001 requirements


Chemical Date of E71T-11

Mechanical    Properties of Deposited Metal of E71T-11
Test Item	Rm(MPa)	ReL or Rp0.2(Mpa)	A(%)	KV2(J)
Guarantee Value	≥480	≥400	≥22	≥27(-20°C)
General Result	580	480	27	128

 

Chemical   Composition of Deposited Metal (%)(CO2Shielding Gas) of E71T-11
Chemical Composition	C	Si	Mn	P	S	Ni	Cu
General Result	0.12	0.04	0.70	0.014	0.011	0.28	0.12

 

Chemical Date of E71T-GS
 

Mechanical    Properties of Deposited Metal of E71T-GS
Test Item	Rm(MPa)	ReL or Rp0.2(Mpa)	A(%)	KV2(J)
Guarantee Value	≥480	≥400	≥22	≥27(-20°C)
General Result	580	480	27	128

 

Chemical    Composition of Deposited Metal (%)(CO2Shielding Gas) of E71T-GS
Chemical Composition	C	Mn	Si	S	P	Ni	Cu
General Result	0.07	0.59	0.06	0.008	0.014	0.25	0.15

 
NOTE ON USAGES:Do not use shielding gas