China Aws A5.18 Er70s-6 CO2 Solid Welding Wires MIG Welding Wire

• Type: MIG Wire
• Material: Mild Steel
• Product Name: Solid Welding Wire
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: ER70S-6
• Surface: Copper Coated or Copper Free
• Packing Type: 5kg/15kg/20kg/250kg/350kg
• Shield Gas: 100% CO2
• Sample: Free Sample
• Specification: 0.6/0.8/0.9/1.0/1.2/1.4/1.6/2.0mm
• Trademark: TYUE
• Origin: China
• HS Code: 722330000
• Production Capacity: 7500000tons/Year
• Package Size: 100.00cm * 100.00cm * 120.00cm
• Package Gross Weight: 15.500kg

Product Description

Product Description
CO2 Mig Welding Wire ER70S-6 Gas Shielded


 MIG welding wire AWS A5.18 ER70S-6,is a kind of carbon steel shielded welding wire. The melting speed of welding wire is fast when welding. It has stable arc, low spatters and beautiful appearance. Good corrosion-resistant on surface of base material. Decrease the probability of blowhole formation. All position welding has good performance CO2 or Ar+CO2 can be used as shielded gas.
 

Detail Information
Product Name:	Cooper Cotaed Welding Wire ER70S-6	Model:	ER70S-6
Brand:	TYUE	Diameter:	0.8/0.9/1.0/1.2/1.6mm
Weight:	5kg/15kg/20kg/250/350kg	Surface:	Cooper Plating
Spool Material:	Black Plastic Spool/steel	Packing:	Color Box/bucket
OEM:	Accept	Diameter Of Spool:	100/200/270/300mm

Confirm with Standard:
GB/T ER50-6/   DIN SG2/     JIS YGW12   
AWS ER70S-6/    BS A18/     EN G3Si1


 
Main Characteristics:
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
 
Application:
AWS A5.18 ER70S-6
1. Used for welding all kinds of 500MPa structural steel parts.
2. Used for welding all kinds of 500MPa plates and pipes.
 
Chemical Composition(%)

Chemical Composition	C	Mn	Si	S	P	Ni	Cr	Mo	V	Cu
Guarantee Value	0.06~0.15	1.40~1.85	0.80~1.15	≤0.025	≤0.025	≤0.15	≤0.15	≤0.15	≤0.03	≤0.50
General Result	0.077	1.45	0.87	0.013	0.012	0.017	0.031	0.002	0.004	0.125

 
Mechanical Properties of Deposited Metal

Test Item	Rm(MPa)	ReL/Rp0.2(MPa)	A(%)	KV2(J)
				-40ºC
Guarantee Value	≥500	≥420	≥22	≥47
General Result	555	450	29	77/95/83

 
Reference Current(DC+)

Size(mm)	Current range (A)	GAS flow rate(L/min)
Φ0.8	50~100	15
Φ1.0	50~220	15~20
Φ1.2	80~350	15~25
Φ1.6	170~550	20~25