TYUE High Cellulose Low Alloy Steel Welding Electrode E8015-G
| Product Name | Low Alloy Steel Electrode | |||||||||
| GB | AWS | JIS | DIN | |||||||
| E5515-G | E8015-G | D5316 | EY5066NiMoBH5 | |||||||
| Type of Covering | Low hydrogen sodium | |||||||||
| Welding Position | F,V, OH,H | |||||||||
| Chemical Composition of Deposited Metal (%) | ||||||||||
| Chemical Composition | C | Mn | Si | S | P | Cr | Ni | Mo | V | Cu |
| Guarantee | - 0.075 |
≥1.00 1.25 |
≥0.80 0.50 |
≤0.03 0.012 |
≤0.03 0.018 |
≥0.30 0.005 |
≥0.50 0.003 |
≥0.20 0.003 |
≥0.10 0.010 |
≥0.20 0.016 |
| Mechanical Properties of Deposited Metal | ||||||||||
| Test Item | Tensile Strengh Rm (MPa) |
Yield point ReL (MPa) |
Elongation A4 (%) |
Akv1(J) | ||||||
| Guarantee | ≥550 590 |
≥460 480 |
≥19 24 |
- -40°C 100 |
||||||
| Reference Current (DC) | ||||||||||
| Electrode Diameter(mm) | 2.5 | 3.2 | 4.0 | 5.0 | ||||||
| Welding Current(A) | 60-90 | 80-110 | 130-170 | 160-200 | ||||||
| Instructions | ||||||||||
| 1.The Electrodes must be baked under 300~350 for an hour before Welding and used as soon as baking is completed. | ||||||||||
| 2.The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away before Welding. | ||||||||||
| 3.When Welding, short arc must be used and stringer bead is suitable. | ||||||||||
| Application | ||||||||||
| Welding medium carbon steel structures and low alloy steel structures. | ||||||||||
R107, AWS E7015-A1, which is used for welding boiler pipes below 510ºC(such as 15Mo). Also used for welding general low-alloy high strength steel.
R207, AWS E8015-B1, which is used for welding CrMo pearlitic heat-resistant steel structures below 510ºC (such as 12Mo), chemical vessels under high temperature and high pressure, etc.
R307, AWS E8015-B2, which is used for welding Cr1%-Mo0.5% heat-resistant steel below 520ºC, such as boiler pipes, high-pressure vessels, equipment for petroleum refining, etc. Also used for welding 30CrMoSi cast steel.
R407, AWS E9015-B3, which is used for welding Cr2.5Mo pearlitic heat-resistant steel structures, such as high-temperature high-pressure pipes below 550ºC, chemical equipment for synthesis, and equipment for petroleum cracking.
W707Ni, AWS E8015-C1, low-temperature steel electrode containing Ni with low-hydrogen natrium type coating. Used for welding of low-temperature steel structures at -70ºC, such as 09Mn2V, 06MnVAl and 3.5 Ni steel, ect. DCRP(Direct Current Reversed Polarity), all-position welding.
Series: ER304, ER308, ER308L, ER309, ER309L, ER316, ER316L, ER410, ER420, ER430etc.
Diameter: 0.6-2.0mm| Packing & Delivery |
| FAQ |
Q: what is delivery time / lead time ?
A: 2-3weeks.
Q: what is your minimum order ?
A: 5000kgs/each size.
Q: what is your payment term ?
A: 50% T/T in advance, 50% balance paid before shipment.
Q: can we visit your factory ?
A: Yes, welcome to our factory at any time.
){kind=link}