Tyue TIG Submerge Arc MIG Welding Wire Em12

• Customization: Available
• Type: Rolling Wire
• Material: Copper / Copper Alloy
• Model NO.: EM12
• Flux Containing: Not Containing Flux
• Slag Characteristic: Acidic
• Extended Length: 10-20mm
• Spool/Reel: D270 / D300
• Transport Package: D200& D270& D300 Plastic Spool+Box+Pallet
• Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
• Trademark: TYUE
• Origin: China
• HS Code: 72292000
• Production Capacity: 1000 Spool

Product Description

Submerge Arc MIG Welding Wire Em12

1. Description: 
1)The weld metal shows a Fine appearance.
2) Both AC and DC can be applied.
3)Stable Arc
4)Easily removable residue

The products easily removable residue, good seam forming and highly efficient deposiyion. Wire meltingdoes not lead to splash or strong flasing. The sem surface is smooth and welding quality is guaranteed. They facilitate mechanical and automatic welding process. With a wide range of welding parameters, the wires can be used in open fields with strong wind and applied to automobiles, ships, and chemical engineering.

Main Applications:
It is suitable to weld 450Mpa-500Mpa grade structures, such as boilers, ships, pressure vessels, as well as LPG cylinders, Before welding, the base metal must clear away impurities and fht flux must be baked in a temperature of 300° C-350° C for 1-2 hours.

Mechanical  Property
Joint  Strength                 (MPA)δ	succumb  strength     (MPA)  δ 0.2	elongation  index                   δ 5%	shock  value             Akv             -20  (J)
560	480	30	105
Chemical  Composition
C	Mn	Si	S	P		Other
0.07%	0.95%	0.03%	0.010%	0.012%		≤ 0.50
Procedure& Package
Dia	2.0mm	2.5mm	3.0mm	3.2mm	4.0mm	5.0mm
Current	300-400	350-450	400-500	425-525	475-575	550-650
Voltage	26-29	27-30	27-30	27-30	27-30	27-30
Weight/spool(KG)	25	25	25	25	25	25