Introduction & Characteristics:
FRW-308L is a rutile type
flux cored wire for low carbon 18%Cr-8%Ni Stainless steel. It is used for all position welding to be used with CO
2or Argon + CO
2 mixed shielding gases.This wire benefits from a fast freezing slag system which assist the operator when welding out of position and performs equally as well when welding in the flat and horizbontal position.
Instructions:
1.The oil stains and rust on the weldments should be cleared away.
2. Designed for welding with CO
2 or Argon + CO
2 mixed shielding gases
3. When welding, the gas flow rate is generally 20~25L/min.
Chemical compostiton of deposited metal (shield gas:CO2)
C |
Mn |
Si |
P |
S |
Ni |
Cr |
0.03 |
1.42 |
0.42 |
0.027 |
0.004 |
9.81 |
19.83 |
Mechanical properties of deposited metal (shield gas:CO2
Yield Strength |
Elongation |
Impact Value |
Mpa(σb) |
%(δ5) |
0ºC(J) |
570 |
43 |
41 |
Sizes available and recommended currents(DC-EP)
Diameter(mm) |
0.9 |
1.2 |
1.6 |
Current(A) |
F,HF |
130-180 |
180-220 |
250-290 |
V-up OH |
100-140 |
120-160 |
220-270 |
Package
Dia(mm) |
1.2 |
1.4 |
1.6 |
Spool(kg)/(lbs) |
5,12.5,15,20/11,28,33 |