Tianyu Brand Cellulose Sodium Coated Type Welding Electrodes/Rods (AWS E6010)

• Customization: Available
• Type: E (Carbon Steel Electrodes/ Low Alloy Steel Electrodes)
• Material: Carbon Steel
• Model NO.: AWS E6010
• Diameter: 1.6mm-5.0mm
• Length: 300-400mm
• Welding Core Type: Carbon Structural Steel
• Electrode Coating Type: High Cellulose Sodium
• Slag Characteristic: Acidic
• Stainless Steel Welding Rod Type: Chromium Nickel Stainless Steel
• Function: High Cellulosic Type Electrode
• Welding Power: DC/AC
• Transport Package: 5kg/Box, 20kg/Carton
• Specification: 1.6mm x 350mm
• Trademark: HAIQIAO
• Origin: China
• HS Code: 831110000
• Production Capacity: 5 Tons
• Package Size: 35.00cm * 23.00cm * 9.50cm
• Package Gross Weight: 5.150kg

Product Description

Description:
E6010 is cellulose Sodium coated type electrode specialized in vertical-down welding of carbon steel. The weld of vertical-down is neat andsmooth. It can be operated on both AC and DC. Less swing and proper level is required when welding.

Application:
It applies to butt welding, fillet welding and overlap welding of thin steel plate such as oil tank of transformer, vessel hull,vehicle crust low carbon steel structure for flue and venting tube.
 

Chemical Composition Deposited Metal (%)
C	Mn	Si	S	P
≤0.12	0.3-0.6	≤0.35	≤0.035	≤0.040

 

Mechanical Properties of Deposited metal
Test Item	Tensile Strength ós (Mpa)	Yield Strength ós (Mpa)	Elongation δ5(%)	Impact Value (J)-30°C
Guranteed	≥420	≥330	≥17	≥27
Tested	480-580	≥340	18-26	100-130

X-ray Radiographic Inspection:  II Grade
 

Sizes & Recommended Current (AC or DC)
Welding rod diameter  (mm)	2.0	2.5	3.2	4.0	5.0
welding current (A)	25-40	30-50	70-100	90-140	150-200

Notes
1.  The defects of less rigidity pars in small thin-wall cast iron pieces can be welded without  preheating, but general weldments need to be preheated up to around 400°C. If the weldmentspreserve heat and slowly cool down, they are on the cards that the soldering joints can bearcut processing.
2.  These welding rods are not suitable for the important castings that bear the stress and impact, etc.
3.  The weld rods should be baked at around 150°C for an hour before the start of welding operation.

  Packing & Delivery

 

 

 

Size: 2.5mm*300mm,
package: 5.0 kg/inner box, 4 boxes/ carton=20kg,

Size: 3.2mm*350mm,
package: 5.0 kg/inner box, 4 boxes/ carton=20kg,

Size: 4.0mm*400mm,
package:5.0 kg/inner box, 4 boxes/ carton=20kg.

1000kgs (50cartons)/pallet

 

   FAQ

 

Q: what is delivery time / lead time ?

A: 2-3weeks.

Q: what is your minimum order ?

A: 5000kgs/each size.

Q: what is your payment term ?

A: 50% T/T in advance, 50% balance paid before shipment.

Q: can we visit your factory ?

A: Yes, welcome to our factory at any time.