Aws E308-16 Welding Rods Low Carbon Stainless Steel Welding Electrodes

• Customization: Available
• Type: L (Low Temperature Low Alloy Steel Electrode)
• Material: Stainless Steel
• Model NO.: E308-16
• Diameter: 1.6mm-5.0mm
• Length: 300-400mm
• Welding Core Type: Stainless Steel
• Electrode Coating Type: Titanium Calcium
• Slag Characteristic: Acidic
• Stainless Steel Welding Rod Type: Chromium Stainless Steel
• Function: Surfacing Electrode, Low Hydrogen Type Electrode, Hardfacing Electrode, High Efficient Iron Powder Electrode, Gravity Electrode, Moisture-Proof Electrode
• Welding Power: DC/AC
• Transport Package: 5kg/Box, 20kg/Carton
• Specification: 1.6MM 2.5MM 3.2MM 4.0MM 5.0MM
• Trademark: TYUE
• Origin: China
• HS Code: 8311100000
• Production Capacity: 10000kg/Day

Product Description

Type: S (Chromium Nickel Austenitic Stainless Steel
Material : Cr19Ni10 Stainless Steel
Diameter: 2.5mm-5.0mm 
Welding Coating: Titaniu Calclum
Application: It is suitable for welding structure of anti-corrosion OCr18Ni9 and OCr18Ni11Ti stainless steel
Working termperature: Below 300 ºC
 

Chemical Composition Deposited Metal (%)
C	Mn	Si	Cr	Ni	S	P	Mo	Cu
≤0.08	0.5-2.5	≤0.90	18-21	9-11	≤0.03	≤0.04	0.75	≤0.75

 

Mechanical Properties of Deposited metal
Test Item	Tensile Strength ós (Mpa)		Elongation δ5(%)
Guranteed	≥550		≥35

The anti-corrosion performance and ferrite composition should be determined between buyer and seller.

Sizes & Recommended Current (AC or DC)
Welding rod diameter  (mm)	2.0	2.5	3.2	4.0	5.0
welding current (A)	25-50	50-80	80-110	110-160	160-200

Notes: 1. Electrodes must be baked for 1 hour at 150ºC before welding operation.
              2.To operate on DC if all possible, because of the penetration is not deep enough. Operate with small current
                 so the electrode will not in red-hot